Semiconductor device and method for manufacturing the same

ABSTRACT

A semiconductor device concerning the embodiment includes a semiconductor layer which has a first surface and a second surface which is opposite to the first surface, an interlayer which is provided on the first surface and which consists of only metal whose standard oxidation-reduction potential is not lower than 0 (zero) V in an ionization tendency, and an electrode provided on the interlayer. The semiconductor device further includes an electrical conductive layer which covers an inside of a hole which is formed in the semiconductor layer so as to reach the interlayer the interlayer from the second surface, and which is electrically connected to the electrode via the interlayer which is exposed to a bottom of the hole.

CROSS-REFERENCE TO RELATED APPLICATION(S)

This application is based upon and claims the benefit of priority fromthe prior Japanese Patent Application No. 2013-032528, filed on Feb. 21,2013, and the prior Japanese Patent Application No. 2013-109204, filedon May 23, 2013, the entire contents of which are incorporated herein byreference.

FIELD

An embodiment relates to a semiconductor device and a method formanufacturing the same.

BACKGROUND

As for a lateral semiconductor device in which current flows in theparallel direction to a surface of a semiconductor layer, an electrodeprovided on a surface of the semiconductor layer and a back electrodeprovided on a back surface of the semiconductor layer are electricallyconnected using a via hole. Thereby, a surface side electrode isgrounded and operation of the semiconductor device is stabilized. Sincea metal layer which is simultaneously formed with an ohmic electrode isgenerally used as the surface side electrode, the surface side electrodeconsists of an alloy layer containing gold germanium (AuGe), nickel (Ni)and gold (Au), and a reaction layer which is formed by reaction of thealloy layer and the semiconductor layer. A hole of the via hole isformed by etching the semiconductor layer selectively using an RIE(Reactive Ion Etching) method, for example. Etching gas containschlorine, for example.

The surface side electrode may deform with the heat at the time ofmounting the semiconductor device on a package or a mounting board, andthereby a contact between the surface side electrode and the backelectrode may become unstable.

The embodiment supplies a reliable semiconductor device in which aconnection between a surface side electrode and a back electrode througha via hole is stable.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A and 1B are schematic diagrams showing a semiconductor deviceconcerning an embodiment;

FIG. 2 is a flow chart showing a manufacture process of thesemiconductor device concerning the embodiment;

FIGS. 3A-3F are schematic sectional views showing the manufactureprocess of the semiconductor device concerning the embodiment; and

FIGS. 4A and 4B are schematic sectional views showing a semiconductordevice concerning a comparative example.

DETAILED DESCRIPTION

According to an embodiment, a semiconductor device includes asemiconductor layer, an interlayer, an electrode provided on theinterlayer, and an electrical conductive layer which is electricallyconnected to the electrode. The semiconductor layer has a first surfaceand a second surface which is opposite to the first surface. Theinterlayer is provided on the first surface, and includes a metal layerconsisting of only metal whose standard oxidation-reduction potential isnot lower than 0 (zero) V in an ionization tendency. The electricalconductive layer covers an inside of a hole which is formed in thesemiconductor layer so as to reach the interlayer from the secondsurface, and is electrically connected to the electrode via theinterlayer which is exposed to a bottom of the hole.

Hereinafter, an embodiment will be explained referring to drawings. Thesame numerals are given to the same portions in the drawings, andoverlapping explanations are omitted.

FIG. 1A and FIG. 1B are schematic diagrams showing a semiconductordevice 1 concerning the embodiment. FIG. 1A is a top view showing a partof the semiconductor device. FIG. 1B is a sectional view taken alongline 1 _(B)-1 _(B) shown in FIG. 1A.

The semiconductor device 1 is a field effect transistor, for example,and is provided with a functional part 7 and a pad electrode 10. Thefunctional part 7 contains source electrodes 3, drain electrodes 4, andgate electrodes 5. As shown in FIG. 1A, the pad electrode 10 isconnected to a plurality of the source electrodes 3.

In addition, as shown in FIG. 1B, the semiconductor device 1 is providedwith a semiconductor layer 20, an electrical conductive layer 30, and aninterlayer 40. The semiconductor layer 20 has a first surface 20 a, anda second surface 20 b that is opposite to the first surface 20 a. Theinterlayer 40 is formed in contact with the first side 20 a of thesemiconductor layer 20. The pad electrode 10 is formed on the interlayer40. Another layer which has conductivity may be provided between the padelectrode 10 and the interlayer 40.

The semiconductor layer 20 has a via hole 17. The via hole 17 includes ahole 17 a which penetrates the semiconductor layer 20 in the directionfacing to the pad electrode 10 from the second surface 20 b and reachesthe interlayer 40 from the second surface 20 b, and a via contact 30 awhich covers an inside of the hole 17 a. The electrical conductive layer30 contains the via contact 30 a and a back electrode 30 b provided onthe second surface 20 a.

The via contact 30 a is in contact with the interlayer 40 which isexposed to a bottom 17 b of the hole 17 a. The interlayer 40 is anelectrical conductive layer containing platinum (Pt), for example, andthe electrical conductive layer 30 is electrically connected to the padelectrode 10 via the interlayer 40.

For example, the interlayer 40 contains a metal layer 13 and a reactionlayer 15 which is formed by reaction of the metal layer 13 and thesemiconductor layer 20. The electrical conductive layer 30 is in contactwith the reaction layer 15. Also, the reaction layer 15 may be removedat the bottom 17 b of the hole 17 and the electrical conductive layer 30may be contact with the metal layer 13 directly. Here, the metal layer13 consists of only metal whose standard oxidation-reduction potentialis not lower than 0 (zero) V in an ionization tendency, for example.

And the interlayer 40 is apart from the functional part 7 which iselectrically connected to the pad electrode 10. That is, the interlayer40 should just be under the pad electrode 10, and does not need to beprovide under the functional part 7 and a part which connects thefunctional part 7 and the pad electrode 10.

Next, a manufacturing method of the semiconductor device 1 is explainedwith reference to FIG. 2 and FIGS. 3A-3F. FIG. 2 is a flow chart showingthe manufacture process of the semiconductor device 1 concerning theembodiment. FIGS. 3A-3F are schematic sectional views showing themanufacture process of the semiconductor device concerning theembodiment. In addition, FIGS. 3A-3F correspond to steps 01-06 shown inFIG. 2 and show partial cross section of a wafer in each step.

To begin with, the metal layer 13 is formed on the first surface 20 a ofthe semiconductor layer 20 as shown in FIG. 3A (S01).

The semiconductor layer 20 is a high resistance layer ofsemi-insulation, and gallium arsenide (GaAs), indium phosphate (InP), orgallium nitride (GaN) can be used as the semiconductor layer 20, forexample. Also, a GaAs board or InP board of semi-insulation may besufficient as the semiconductor layer 20.

The metal layer 13 is selectively formed on a part of the semiconductorlayer 20 on which the pad electrode 10 is formed. The metal layer 13 isdesirable to have tolerance for the dry etching which is used forformation of the hole 17 a for the via hole 17. That is, a metal whichis chemically stable and does not react to the active element containedin an etching gas is used as the metal layer 13. The etching gascontains chlorine when the semiconductor layer 20 is a GaAs layer or anInP layer, for example. Therefore, it is preferable to use platinum (Pt)which is stable chemically to chlorine as the metal layer 13.

On the other hand, the specific resistance of platinum is larger thanthe specific resistance of gold (Au) which is used for the pad electrode10. For this reason, as for the thickness of the metal layer 13, it isdesirable that it is not larger than 60 nm, for example.

Next, as shown in FIG. 3B, by adding heat treatment to the semiconductorlayer 20 and the metal layer 13, the semiconductor layer 20 and themetal layer 13 react to thereby form the reaction layer 15 (S02).

When the metal layer 13 is a platinum layer, the reaction layer 15containing platinum is formed between the semiconductor layer 20 and themetal layer 13.

Next, as shown in FIG. 3C, the pad electrode 10 is formed on the metallayer 13 (S03). The pad electrode 10 is a source pad, for example, andis formed so as to be connected to the source electrodes 3. An Au layercan be used as the pad electrode 10, for example.

Next, as shown in FIG. 3D, the semiconductor layer 20 is thinned (S04).When a GaAs board or an InP board is used as the semiconductor layer 20,for example, the semiconductor layer 20 is thinned to thickness ofseveral 10 μm by grinding or polishing. In addition, an epitaxiallygrown layer separated from a growth board may be used as thesemiconductor layer 20.

Next, as shown in FIG. 3E, the hole 17 a is formed in the directionwhich faces to the pad electrode 10 from the second surface 20 b of thesemiconductor layer 20 which has been thinned (S05). The semiconductorlayer 20 is selectively etched using the RIE (Reactive Ion Etching)method, for example, to thereby form the hole 17 a. An etching gascontains chlorine, for example.

The hole 17 a reaches either of the reaction layer 15 and the metallayers 13. For example, when a platinum layer is used for the metallayer 13, the reaction layer 15 contains platinum. The etching rate ofthe reaction layer 15 becomes lower than the etching rate of thesemiconductor layer 20. Thereby, it becomes easy to stop etching at thereaction layer 15. That is, the reaction layer 15 can be exposed to thesecond surface side of the semiconductor layer 20. Also, the reactionlayer 15 may be removed to thereby expose the metal layer 13.

Next, as shown in FIG. 3F, the electrical conductive layer 30 whichcovers the inside of the hole 17 a is formed and thereby the via hole 17is formed (S06). The electrical conductive layer 30 is a gold platelayer, for example. A seed layer 21 is formed on the inside of the hole17 a and the second surface 20 b, for example. Then, electrolyticplating of gold is performed while flowing current through the seedlayer 21 and a gold plate layer is formed on the seed layer 21. Atwo-layer film in which titanium (Ti) and gold (Au) are laminated inorder from the semiconductor layer 20 side can be used as the seed layer21, for example. Ti film raises the adhesion power between thesemiconductor layer 20 and the electrical conductive layer 30, andraises the adhesion power between the reaction layer 15 and theelectrical conductive layer 30.

The above-mentioned manufacture process can form a via-structure whichelectrically connects the pad electrode 10 provided on first surface 20a of the semiconductor layer 20 and the electrical conductive layer 30provided in the second surface 20 b side.

FIGS. 4A and 4B are schematic sectional views showing a semiconductordevice 2 concerning a comparative example. FIG. 4A shows a cross section(refer to FIG. 1B) taken along an I_(B)-I_(B) line. FIG. 4B is anenlarged drawing of a part A shown in FIG. 4A, and shows a connectionstructure between the pad electrode 10 and the electrical conductivelayer 30.

The semiconductor device 2 includes a metal layer 23 and a reactionlayer 25. The metal layer 23 contains a metal whose standardoxidation-reduction potential is lower than 0 (zero) V in an ionizationtendency, for example. Accordingly, the reaction layer 25 contains ametal whose standard oxidation-reduction potential is lower than 0(zero) V in an ionization tendency, for example.

The metal layer 23 contains gold germanium (AuGe), nickel (nickel) andgold (Au) which were laminated in order from the semiconductor layer 20side, for example, because the semiconductor device 2 uses a metal layerwhich is simultaneously formed with the ohmic electrode as a surfaceside electrode. That is, the metal layer 23 contains nickel which reactschemically with chlorine. And the reaction layer 25 which is formed byheat-treating the metal layer 23 and the semiconductor layer 20 alsocontains nickel.

Also in this comparative example, the semiconductor layer 20 is etchedin the direction which faces to the pad electrode 10 from the secondsurface 20 b of the semiconductor layer 20 by dry etching and therebythe hole 17 a is formed. And the reaction layer 25 is exposed to thesecond surface 20 b side. At this time, nickel contained in the reactionlayer 25 reacts with chlorine contained in an etching gas, and therebychlorination nickel (NiCl2) is produced on an exposed surface of thereaction layer 25.

Chlorination nickel corrodes the reaction layer 25 in the formationprocess of the electrical conductive layer 30, and forms voids 31 in thesurface of the reaction layer 25 as shown in FIG. 4B. And plating liquidenters into the voids 31 in the process of gold-plating which forms anelectrical conductive layer 30, and the plating liquid may remain in thevoid 31 as it is.

When the semiconductor device 2 is heated in a case that thesemiconductor device 2 is mounted on a package or a mounting board, theplating liquid which remains inside the void 31 evaporate to therebyraise the internal pressure of the void 31. For this reason, thephenomenon in which the reaction layer 25 is dissociated from theelectrical conductive layer 30, and in which the reaction layer 25, themetal layer 23 and pad electrode 10 are inflated occurs. As a result, anelectrical connection between the electrical conductive layer 30 and thepad electrode 10 may be lost, and operation of the semiconductor device2 may become unstable.

On the other hand, according to the embodiment, the metal layer 13 ischemically stable to chlorine contained in the etching gas. That is, themetal layer 13 does not contain any element that reacts with the activeelement contained in the etching gas. Even if the metal layer 13contains such an element that reacts with the active element containedin the etching gas, the concentration of such element is not higher thana level detectable using the measuring means, such as an SIMS (SecondaryIon Mass Spectrometry) and a Auger spectroscopy.

Also the reaction layer 15 that is formed by reaction of the metal layer13 and the semiconductor layer 20 does not contain any unstable elementto chlorine contained in the etching gas. For this reason, the void 31is not formed between the reaction layer 15 and the electricalconductive layer 30, and deformation of the reaction layer 15, the metallayer 13 and the pad electrode 10 can be suppressed. And the electricalconnection between the electrical conductive layer 30 and the padelectrode 10 is held stable, and the reliability of the semiconductordevice can be improved.

A metal which is chemically unstable to chlorine contained in theetching gas is metal whose standard oxidation-reduction potential islower than 0 (zero) V in an ionization tendency. Aluminum (Al), titanium(Ti), tantalum (Ta), chromium (Cr), nickel (nickel), tin (Sn), etc. outof the metals used in a semiconductor process in many cases, correspondto such a metal.

A metal which is chemically stable to chlorine contained in the etchinggas is a metal whose standard oxidation-reduction potential is not lowerthan 0 (zero) V in an ionization tendency. Copper (Cu), palladium (Pd),platinum (Pt), gold (Au), etc. out of the metals used in a semiconductorprocess in many cases, correspond to such a metal.

While the embodiment has been described, the embodiment has beenpresented by way of example only, and is not intended to limit the scopeof the inventions. Indeed, the novel embodiment described herein may beembodied in a variety of other forms; furthermore, various omissions,substitutions and changes in the form of the embodiment described hereinmay be made without departing from the spirit of the inventions. Theaccompanying claims and their equivalents are intended to cover suchforms or modifications as would fall within the scope and spirit of theinventions.

What is claimed is:
 1. A semiconductor device, comprising: asemiconductor layer which has a first surface and a second surface whichis opposite to the first surface; an interlayer which is provided on thefirst surface, and which includes a metal layer consisting of only metalwhose standard oxidation-reduction potential is not lower than 0 (zero)V in an ionization tendency; an electrode provided on the interlayer;and an electrical conductive layer which covers an inside of a holewhich is formed in the semiconductor layer so as to reach the interlayerfrom the second surface, and which is electrically connected to theelectrode via the interlayer which is exposed to a bottom of the hole.2. The semiconductor device according to claim 1, wherein the metallayer of the interlayer consists of platinum (Pt).
 3. The semiconductordevice according to claim 1, wherein the metal layer of the interlayerconsists of one metal or plural metals selected from a group consistingof copper (Cu), palladium (Pd), platinum (Pt), and gold (Au).
 4. Thesemiconductor device according to claim 1, wherein the interlayercontains the metal layer and a reaction layer which is formed byreaction of the metal layer and the semiconductor layer, and theelectrical conductive layer is in contact with the reaction layer. 5.The semiconductor device according to claim 4, wherein the interlayercontains a platinum layer and the reaction layer which is formed byreaction of the platinum layer and the semiconductor layer, and theelectrical conductive layer is in contact with the reaction layer. 6.The semiconductor device according to claim 1, further comprising afunctional part which is electrically connected to the electrode, andwherein the interlayer is separated from the functional part.
 7. Amethod for manufacturing a semiconductor device, comprising: forming ametal layer consisting of only metal whose standard oxidation-reductionpotential is not lower than 0 (zero) V in an ionization tendency on afirst surface of a semiconductor layer; forming a reaction layer byheat-treating the metal layer and the semiconductor layer; forming anelectrode on the metal layer; exposing at least one of the reactionlayer and the metal layer to the second surface of the semiconductorlayer which is opposite to the first surface by forming a hole whichpenetrates the semiconductor layer in the direction facing to theelectrode from the second surface; and forming an electrical conductivelayer which covers the inside of the hole and is electrically connectedto the electrode.
 8. The method for making semiconductor deviceaccording to claim 7, wherein the metal layer is a platinum layer.